RINA FH36 Shipbuilding Steel Plate, Hot Rolled Steel Plate 2mm - 200mm Thickness
RINA FH36 Shipbuilding Steel Plate, Hot Rolled Steel Plate 2mm - 200mm Thickness
RINA FH36 Shipbuilding Steel Plate, Hot Rolled Steel Plate 2mm - 200mm Thickness
RINA FH36 Shipbuilding Steel Plate, Hot Rolled Steel Plate 2mm - 200mm Thickness
RINA FH36 Shipbuilding Steel Plate, Hot Rolled Steel Plate 2mm - 200mm Thickness
RINA FH36 plak asye konstriksyon bato, plak asye cho woule 2mm - 200mm epesè
Kòm yon founisè dirijan ak manifakti nan Lachin, GNEE Steel bay pri -efikas nikèl-pwodwi alyaj ki baze sou.
- Voye imèl -:ss@gneesteel.com
- Tel:+8615824687445
RINA FH36 plak asye konstriksyon bato, plak asye woule cho 2mm - 200mm epesè
Deskripsyon
| Non: | Bato Steel Plak | Materyèl: | ADEF Klas |
|---|---|---|---|
| Longè: | 6-11m | Lajè: | {{0}mm |
| Epesè: | {{0}mm | Kalite: | Woule cho |
| Limyè segondè: |
plak anbake,plak asye maren |
||
RINA FH36 plak asye konstriksyon bato, F36 bato asye, cho plak asye woule pou estrikti bato
ekipman pou klas asye RI/A36, RI/D36, RI/EH36, RI/F36, RI/A32, RI/D32, RI/E32, RI/F32, RI/A, RI/B, RI/D,RI/E . RI/A40, RI/D40, RI/E40, RI/F40.
FH36 se yon gwo fòs bato asye klas, nan -60 charpy V enpak ak estasyon livrezon nòmalize pou konstriksyon bato. Abityèl epesè max se 100mm, men pwofesyonèl konpayi nou an tou ta ka bay plak asye super epè ki pi lwen pase Sosyete Klasifikasyon Otantifye.
Deskripsyon
|
Non |
bato bati plak asye AH32, AH36, AH40 |
|
Spesifikasyon |
kòm kondisyon ou |
|
Epesè |
2mm ~ 200mm |
|
Lajè |
500mm ~ 3000mm |
|
Longè |
2000mm-18000mm (tankou kondisyon ou) |
|
teknik fabrikasyon |
Woule cho |
|
Tretman sifas yo |
kouvwi |
|
Estanda |
ASTRA |
|
aplikasyon |
bato bati plak asye |
|
Anbalaj |
Creole ekspòte anbalaj oswa kòm kondisyon kliyan an |
|
Sètifika |
Rapò Tès Kalite / ISO9001: 2008 / Sètifika tès Mill |
|
Pi wo a se atik jeneral yo, pou kalite espesyal yo, nou kapab tou satisfè bezwen ou yo |
|
Konsènan enfòmasyon detaye FH36, tanpri tcheke dat teknik ki annapre yo.
Chimik la se konpozisyon maksimòm analiz pwodwi:
|
Klas |
C % |
Si % |
Mn % |
P % |
S % |
V % |
AL % |
% Cr |
|
FH36 |
0.160 |
0.10-0.5 |
0.9-1.6 |
0.025 |
0.025 |
0.05-0.10 |
0.015 |
0.200 |
|
Cu % |
Mo % |
Nb % 25 |
Ni % |
Ti % |
N % |
|
|
|
|
0.350 |
0.080 |
0.02-0.05 |
0.080 |
0.020 |
0.012 |
|
|
Pwopriyete mekanik yo nan tanperati anbyen pou plak asye trempe ak apeze
|
Klas |
Epesè (mm) |
Sede Minim (Mpa) |
Tensile (MPa) |
elongasyon (%) |
Enèji enpak min |
|
|
FH36 |
8mm{{1}mm |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
34J |
|
51mm{{1}m |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
nati |
|
|
71mm{{1}mm |
Min 355Mpa |
490-620Mpa |
21% |
-60 |
nati |
|
|
Enèji enpak min se enèji longitudinal |
||||||
FH36 moulen nou an toujou ekspòte nan Singapore ak Thailand chantye bato pou konstriksyon bato.
Pou jwenn sitasyon konpetitif nou an, tanpri ou lib pou kontakte nou.