Klas ekivalan Inconel 600 ak Inconel 625
| Klas ekivalan | INCONEL 625 | INCONEL 600 |
|---|---|---|
| EN – DIN | NiCr 22 Mo 9 Nb | NiCr 15 Fe |
| ASTM - UNS | N06625 | N06600 |
| W. Nr | 2.4856 | 2.4816 |
| AFNOR | NC 22 DNb | NC 15 Fe 7 TA |
Konparezon Pwopriyete Inconel ak Monal
| Pwopriyete | Inconel | Monal | ||
|---|---|---|---|---|
| INCONEL 625 | INCONEL 600 | Monal 400 | ||
| Pwopriyete mekanik | Allongement nan Break | 3.4 a 35% | 33 a 34% | 20 a 40% |
| Pwopòsyon Poisson a | 0.29 | 0.29 | 0.32 | |
| Chea fòs | 430 a 570 MPa (62 a 83 x 103psi) | 530 a 600 MPa (77 a 87 x 103psi) | 370 a 490 MPa (53 a 71 x 103psi) | |
| Chea modil | 75 GPa (11 x 106psi) | 79 GPa (11 x 106psi) | 62 GPa (9.0 x 106psi) | |
| Pwopriyete tèmik | Tanperati Curie | -120 degre (-190 degre F) | -200 degre (-320 degre F) | 40 degre (100 degre F) |
| Chalè Inaktif nan Fusion | 310 J/g | 330 J/g | 270 J/g | |
Jwenn diferans ki genyen ant Inconel ak Nerjaveèi anba a
Pwopriyete Inconel ak Nerjaveèi
| Pwopriyete | Inconel | Nerjaveèi asye | ||||
|---|---|---|---|---|---|---|
| INCONEL 625 | INCONEL 600 | AISI 304 | AISI 316 | AISI 410 | ||
| Pwopriyete mekanik | Modil elastik | 190 GPa (28 x 106psi) | 200 GPa (30 x 106psi) | 200 GPa (29 x 106psi) | 200 GPa (29 x 106psi) | 190 GPa (28 x 106psi) |
| Fòs fatig | 220 a 300 MPa (32 a 44 x 103psi) | 240 a 320 MPa (34 a 47 x 103psi) | 210 a 440 MPa (30 a 63 x 103psi) | 210 a 430 MPa (30 a 63 x 103psi) | 190 a 350 MPa (28 a 50 x 103psi) | |
| Fòs rupture | 650 a 990 MPa (94 a 140 x 103psi) | 790 a 910 MPa (120 a 130 x 103psi) | 580 a 118 0MPa (84 a 170 x 103psi) | 520 a 118 0MPa (76 a 170 x 103psi) | 520 a 770 MPa (76 a 110 x 103psi) | |
| Sede fòs | 270 a 760 MPa (39 a 110 x 103psi) | 320 a 450 MPa (47 a 65 x 103psi) | 230 a 860 MPa (34 a 120 x 103psi) | 230 a 850 MPa (33 a 120 x 103psi) | 290 a 580 MPa (42 a 84 x 103psi) | |
| Pwopriyete tèmik | Kapasite Chalè Espesifik | 460J/kg-K (0.11BTU/lb- degre F) | 440J/kg-K (0.1BTU/lb- degre F) | 480J/kg-K (0.11BTU/lb- degre F) | 470J/kg-K (0.11BTU/lb- degre F) | 480J/kg-K (0.11BTU/lb- degre F) |
| Ekspansyon tèmik | 13µm/m-K | 13µm/m-K | 17µm/m-K | 16µm/m-K | 11µm/m-K | |
| Kondiktivite tèmik | 14W/m-K (8.2BTU/h-pye- degre F) | 11W/m-K (6.4BTU/h-pye- degre F) | 16W/m-K (9.2BTU/h-pye{- degre F) | 15W/m-K (8.9BTU/h-pye{- degre F) | 30W/m-K (17BTU/h-pye{- degre F) | |
Aplikasyon ki gen bon konprann diferans ant alyaj 600 ak 625
| Aplikasyon | Inconel 600 | Inconel 625 | |
|---|---|---|---|
| Itilizasyon Tanperati segondè- |  |
Konpozan founo chalè -trete ekipman |
Motè jè plak pwotèj chalè sistèm tiyo echapman |
| Pwosesis chimik |  |
Echanjeur chalè evaporatè turbin gaz |
Scrubbers asid sistèm kontwòl polisyon |
| Aplikasyon Marin |  |
Pa souvan itilize |
Tiyo dlo lanmè ekipman anba lanmè |
| Jenerasyon pouvwa |  |
Konpozan réacteurs dèlko vapè |
Epurasyon gaz lafimen echanjeur chalè liy vapè |
| Jeneral Endistriyèl |  |
Pwosesis manje chofaj endistriyèl |
Min pétrochimique ekstrèm durability |
Konpozisyon chimik Nikèl 600 & 625
| Pwopriyete | INCONEL 625 | INCONEL 600 |
|---|---|---|
| Souf (S) | 0 a 0.015 | 0 a 0.015 |
| Kabòn (C) | 0 a 0.1 | 0 a 0.15 |
| Aliminyòm (Al) | 0 a 0.4 | - |
| Manganèz (Mn) | 0 a 0.5 | 0 a 1.0 |
| Fè (Fe) | 0 a 5.0 | 6.0 a 10 |
| Molybdène (Mo) | 8.0 a 10 | - |
| Nikèl (Ni) | 58 a 68.9 | 72 a 80 |
| Kwòm (Cr) | 20 pou 23 | 14 pou 17 |
| Niobyòm (Nb) | 3.2 a 4.2 | - |
| Cobalt (Ko) | 0 a 1.0 | - |
| Silisyòm (Si) | 0 a 0.5 | 0 a 0.5 |
| Titàn (Ti) | 0 a 0.4 | - |
| Fosfò (P) | 0 a 0.015 | - |
| Kwiv (Cu) | - | 0 a 0.5 |
Inconel 600 & 625 Round Bar pwa pou chak mèt
| INCONEL 600 BAR WONT | |
| Dyamèt mm | KG P/Mtr |
|---|---|
| 80 | 42.88 |
| 50.8 | 17.29 |
| 22.23 | 3.31 |
| 9.53 | 0.61 |
| 75 | 37.69 |
| 44.45 | 13.24 |
| 20 | 2.68 |
| 160 | 171.52 |
| 63.5 | 27.02 |
| 38.1 | 9.73 |
| 19.05 | 2.43 |
| 130 | 113.23 |
| 57.15 | 21.88 |
| 25 | 4.19 |
| 12.7 | 1.08 |
| 12.7 | 1.08 |
| INCONEL 625 BÒ WONT | |
|---|---|
| Dyamèt mm | KG P/Mtr |
| 101.6 (4") | 68.42 |
| 50.8 (2") | 38.49 |
| 31.75 (1-1/4") | 6.68 |
| 100 | 66.28 |
| 50 | 16.57 |
| 16 | 1.7 |
| 203 | 273.15 |
| 76.2 (3") | 38.49 |
| 40 | 10.61 |
| 114.3 (4-1/2") | 86.6 |
| 70 | 32.48 |
| 35 | 8.12 |
Inco 625 vs 600 Pwopriyete
| Pwopriyete | Rekwit Inconel 625 | Solisyon trete 625 |
|---|---|---|
| Allongement nan Break | 33% | 34% |
| Pwopòsyon Poisson a | 0.29 | 0.29 |
| Chea fòs | 600 MPa (87 x 103psi) | 530 MPa (77 x 103psi) |
| Sede fòs | 450 MPa (65 x 103psi) | 320 MPa (47 x 103psi) |
| Modil elastik | 200 GPa (30 x 106psi) | 200 GPa (30 x 106psi) |
| Fòs fatig | 320 MPa (47 x 103psi) | 240 MPa (34 x 103psi) |
| Chea modil | 79 GPa (11 x 106psi) | 79 GPa (11 x 106psi) |
| Fòs Tensile: Ultim (UTS) | 910 MPa (130 x 103psi) | 790 MPa (120 x 103psi) |
| Mekanik | 980 degre (1800 degre F) | 980 degre (1800 degre F) |
| Aparisyon k ap fonn | 1290 degre (2350 degre F) | 1290 degre (2350 degre F) |
| Kondiktivite tèmik | 11 W/m-K (6.4 BTU/h-pye- degre F) | 11 W/m-K (6.4 BTU/h-pye- degre F) |
| Chalè Inaktif nan Fusion | 330 J/g | 330 J/g |
| Fini fonn | 1350 degre (2460 degre F) | 1350 degre (2460 degre F) |
| Kapasite Chalè Espesifik | 440 J/kg-K (0.1 BTU/lb- degre F) | 440 J/kg-K (0.1 BTU/lb- degre F) |
| Ekspansyon tèmik | 13 µm/m-K | 13 µm/m-K |
| Tanperati Curie | -200 degre (-320 degre F) | -200 degre (-320 degre F) |
| Molybdène | 8.0 a 10 | 8.0 a 10 |
| Fè | 0 a 5.0 | 0 a 5.0 |
| Manganèz | 0 a 0.5 | 0 a 0.5 |
| Aliminyòm | 0 a 0.4 | 0 a 0.4 |
| Kabòn | 0 a 0.1 | 0 a 0.1 |
| Souf | 0 a 0.015 | 0 a 0.015 |
| Kwòm | 20 pou 23 | 20 pou 23 |
| Niobyòm | 3.2 a 4.2 | 3.2 a 4.2 |
| Cobalt | 0 a 1.0 | 0 a 1.0 |
| Silisyòm | 0 a 0.5 | 0 a 0.5 |
| Titàn | 0 a 0.4 | 0 a 0.4 |
| Fosfò | 0 a 0.015 | 0 a 0.015 |
| Nikèl | 58 a 68.9 | 58 a 68.9 |
Nikèl alyaj 600 & 625 Tanperati Range
| Klas | Tretman Chalè | Ranje Tanperati |
|---|---|---|
| 600 | Rkwit | 1350 degre (2470 degre F) |
| 600 | Plen-Difisil | 1350 degre (2470 degre F) |
| 600 | Mwatye-Difisil | 1350 degre (2470 degre F) |
| 600 | Cho travay | 1350 degre (2470 degre F) |
| 625 | Rkwit | 1290 degre (2350 degre F) |
| 625 | Solisyon trete | 1290 degre (2350 degre F) |
Alloy 600 vs 625 Pwen k ap fonn
| Klas | Tretman Chalè | Aparisyon k ap fonn | Fini fonn |
|---|---|---|---|
| 600 | Rkwit | 1350 degre (2470 degre F) | 1410 degre (2580 degre F) |
| 600 | Plen-Difisil | 1350 degre (2470 degre F) | 1410 degre (2580 degre F) |
| 600 | Mwatye-Difisil | 1350 degre (2470 degre F) | 1410 degre (2580 degre F) |
| 600 | Cho travay | 1350 degre (2470 degre F) | 1410 degre (2580 degre F) |
| 625 | Rkwit | 1290 degre (2350 degre F) | 1350 degre (2460 degre F) |
| 625 | Solisyon trete | 1290 degre (2350 degre F) | 1350 degre (2460 degre F) |
Nikèl 600 vs 625 dite HRC
| Materyèl | Dite, Rockwell |
|---|---|
| Alyaj 600 baton ak ba | 65-85B |
| Alloy 600 Plak | 65-85B |
| Alloy 600 Fèy | 88B max |
| Alyaj 625 Bar | Mwens pase oswa egal a 287 HB |
| Alloy 625 Fèy | 145-240 |
In625 vs 600 Dansite
| Klas | Tretman Chalè | Dansite |
|---|---|---|
| 600 | Rkwit | 8.5 g/cm3530 lb/pye3 |
| 600 | Plen-Difisil | 8.5 g/cm3530 lb/pye3 |
| 600 | Mwatye-Difisil | 8.5 g/cm3530 lb/pye3 |
| 600 | Cho travay | 8.5 g/cm3530 lb/pye3 |
| 625 | Rkwit | 8.6 g/cm3540 lb/pye3 |
| 625 | Solisyon trete | 8.6 g/cm3540 lb/pye3 |
Gamme pwodwi nou an
| Fòm pwodwi | Espesifikasyon estanda ak dimansyon | Alyaj komen (Egzanp) | Estanda tipik |
|---|---|---|---|
| Bar & Rod | Bar wonn:Dyamèt: 3mm ~ 300mm Egzagòn Bar:Atravè plat: 5mm ~ 100mm Bar kare:Lajè: 5mm ~ 150mm Longè:Owaza, Koupe-a-longè, oswa Bobin (ti dyamèt) |
Alyaj 200/201 Monel 400/K-500 Inconel 600/601/625/718 Incoloy 800/800H/825 Hastelloy C-276/C-22/B-2/B-3 |
ASTM B160, B164, B166 EN/DIN 2.4066, 2.4816, 2.4851 ASME SB-166, SB-167 |
| Fil | Dyamèt:0.1mm ~ 12mm Fòm:Bobin, bobin, oswa longè dwat Fini:Bright, marinated, rkwit |
Alyaj 200/201 Inconel 600/625/X-750 Incoloy 825 |
ASTM B166, B167 EN/DIN 17752 |
| Fèy & Plak | Epesè (fèy):0.1mm ~ 5.0mm Epesè (plak):5.0mm ~ 100mm + Lajè:Jiska 2000mm (depann sou alyaj / epesè) Longè:Jiska 6000mm oswa jan sa nesesè |
Alyaj 200/201 Monel 400 Inconel 600/625/718 Incoloy 800H/825 Hastelloy C-276 |
ASTM B162, B168, B409 EN/DIN 17742, 17744 |
| Strip & Foil | Epesè (Bay):0.05mm ~ 2.0mm Epesè (FOIL):0.02mm ~ 0.05mm Lajè:Jiska 600mm Kondisyon:Fwad woule, rkwit, apeze |
Alyaj 200/201 Inconel 600/625 Incoloy 825 |
ASTM B162, B168 |
| Tiyo & Tib | Tiyo san pwoblèm (ASTM B161/B167): - OD: 3/16" ~ 14" (6mm ~ 355mm) - Orè: SCH 5S rive XXS Tib soude (ASTM B163/B516): - OD: 6mm ~ 300mm - Mi epesè: 0.5mm ~ 10mm |
Alyaj 200/201 Monel 400 Inconel 600/625 Incoloy 800H/825 Hastelloy C-276 |
ASTM B161, B163, B167, B516 ASME SB-163, SB-167 |
Faktori nou yo ak tès yo
Faktori debaz nou an ak sistèm pwodiksyon kolaborasyon yo ekipe ak ekipman modèn koupe presizyon, pwosesis, ak tretman chalè, konsantre sou transfòme matyè premyè nan pwodwi semi-fini ak fini ki satisfè estanda sevè. Pou asire ke chak pakèt materyèl satisfè oswa depase espesifikasyon yo, nou te etabli yon konplè fen-a-sistèm enspeksyon kalite. Soti nan analiz pwopriyete materyèl (PMI) sou depo materyèl anvan tout koreksyon nan kontwòl presizyon dimansyon pandan pwodiksyon, epi finalman nan tès pwopriyete mekanik (tankou fòs rupture ak dite) ak tès ki pa -destriktif anvan chajman final la, chak etap se rigoureman kontwole pa ekip pwofesyonèl enspeksyon kalite nou an. Nou pwomèt pou nou bay yon sètifika materyèl fabrikan orijinal ki otorize, -verifiyab sou Entènèt (MTC 3.1) pou chak lòd, epi nou ka fè aranjman pou yon twazyèm pati -kò sètifikasyon (tankou SGS, BV, ak TUV) fè enspeksyon sou sit- epi bay sètifika sou demann kliyan an.